| Technical Specification |
CMI-7000S |
| Single Sheet |
| Functionality |
Strong Acid
Cation Exchange Membrane |
| Polymer Structure |
Gel polystyrene
cross linked with divinylbenzene |
| Functional Group |
Sulphonic Acid |
| Ionic Form as Shipped |
Sodium |
| Color |
Brown |
| Standard Size |
: US |
| |
: Metric |
|
48in x 120in
1.2m x 3.1m |
| Standard Thickness | (mils)
(mm) |
|
18±1
0.45±0.025 |
Electrical Resistance (Ohm.cm2)
0.5 mol/L NaCl |
<30 |
Permselectivity (%)
0.1 mol KCl/kg / 0.5 mol KCl/kg |
94 |
| Total Exchange Capacity (meq/g) |
1.6±0.1 |
Water Permeability
(ml/hr/ft2) @5psi |
<3 |
| Mullen Burst Test strength (psi) |
>80 |
| Thermal Stability (oC) |
90 |
| Chemical Stability Range (pH) |
1-10 |
| Preconditioning Procedure |
Membranes should be preconditioned by emersion in a 5% NaCl solution at 40oC for 24 hours to allow for membrane hydration and expansion. |